Preparation andproperty of HKT800 carbon fiber/AG80 epoxy resin composite

	Preparation andproperty of HKT800 carbon fiber/AG80 epoxy resin composite
其他题名	HKT800碳纤维/AG80环氧树脂复合材料制备及性能
	Gu, Hongxing; Wang, Haojing; Fan, Lidong; Zhang, Shubin; Pang, Peidong
	2015-08-15
发表期刊	Gongneng Cailiao/Journal of Functional Materials
卷号	46 期号:15 页码:15007-15010
摘要	The surface topography, elements, functional groups of HKT800 carbon fiber were characterized, the recipe of AG80 epoxy resin was optimized, then the mechanical and interface performance of HKT800 carbon fiber/AG80 epoxy resin composite were analyzed. The results showed that: the ratio of O/C and N/C in surface elements reached 25.2% and 4.5%, the ratio of active carbon atoms was 0.91, so the surface activity of HKT800 carbon fiber was higher. The epoxy resin could be cured at 150 when the mass ratio of AG80, DDS, BF3·MEA was 100:30:3. The tensile, flexural and compression strength of HKT800 carbon fiber/AG80 epoxy resin composite were 2 682, 1 874 and 1 639 MPa, interlayer shear strength was 110 MPa. ©, 2015, Journal of Functional Materials. All right reserved.
收录类别	EI
语种	中文
文献类型	期刊论文
条目标识符	http://ir.opt.ac.cn/handle/181661/27350
专题	复合材料与器件先进制造研发中心
推荐引用方式 GB/T 7714	Gu, Hongxing,Wang, Haojing,Fan, Lidong,et al. Preparation andproperty of HKT800 carbon fiber/AG80 epoxy resin composite[J]. Gongneng Cailiao/Journal of Functional Materials,2015,46(15):15007-15010.
APA	Gu, Hongxing,Wang, Haojing,Fan, Lidong,Zhang, Shubin,&Pang, Peidong.(2015).Preparation andproperty of HKT800 carbon fiber/AG80 epoxy resin composite.Gongneng Cailiao/Journal of Functional Materials,46(15),15007-15010.
MLA	Gu, Hongxing,et al."Preparation andproperty of HKT800 carbon fiber/AG80 epoxy resin composite".Gongneng Cailiao/Journal of Functional Materials 46.15(2015):15007-15010.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Preparation andprope（332KB）	期刊论文	作者接受稿	限制开放	CC BY-NC-SA	请求全文