Faraday Glasses with a Large Size and High Performance
Li, Weinan; Zou, Kuaisheng; Lu, Min; Peng, Bo; Zhao, Wei
2010
发表期刊INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY
ISSN1744-7402
卷号7期号:3页码:369-374
摘要A kind of Faraday glass with a size of 40 mm x 14 mm and 100-300 mm x 25 mm, respectively, was prepared by the melting and casting process, which had neither a Pt particulate nor a bubble or striation. The measurement results showed that the surface homogeneity of the samples was up to +/- 1 x 10-6, the laser threshold reached 10 J/cm2 (1 omega, 3 ns), and the Verdet constants of the glasses were -0.273 min/Oe/cm at 632.8 nm and -0.076 min/Oe/cm at 1064 nm, respectively.
文章类型Article
WOS标题词Science & Technology ; Technology
DOI10.1111/j.1744-7402.2008.02344.x
收录类别SCI ; EI
关键词[WOS]REFRACTIVE-INDEX ; MAGNETIC-FIELD ; OXIDE GLASSES ; ROTATION ; DEPENDENCE
语种英语
WOS研究方向Materials Science
WOS类目Materials Science, Ceramics
WOS记录号WOS:000277291900010
引用统计
被引频次:20[WOS]   [WOS记录]     [WOS相关记录]
文献类型期刊论文
条目标识符http://ir.opt.ac.cn/handle/181661/8430
专题光子功能材料与器件研究室
作者单位Chinese Acad Sci, State Key Lab Transient Opt & Photon, Xian Inst Opt & Proc Mech, Xian, Peoples R China
推荐引用方式
GB/T 7714
Li, Weinan,Zou, Kuaisheng,Lu, Min,et al. Faraday Glasses with a Large Size and High Performance[J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,2010,7(3):369-374.
APA Li, Weinan,Zou, Kuaisheng,Lu, Min,Peng, Bo,&Zhao, Wei.(2010).Faraday Glasses with a Large Size and High Performance.INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,7(3),369-374.
MLA Li, Weinan,et al."Faraday Glasses with a Large Size and High Performance".INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY 7.3(2010):369-374.
条目包含的文件
文件名称/大小 文献类型 版本类型 开放类型 使用许可
Faraday Glasses with(429KB)期刊论文出版稿限制开放CC BY-NC-SA请求全文
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Li, Weinan]的文章
[Zou, Kuaisheng]的文章
[Lu, Min]的文章
百度学术
百度学术中相似的文章
[Li, Weinan]的文章
[Zou, Kuaisheng]的文章
[Lu, Min]的文章
必应学术
必应学术中相似的文章
[Li, Weinan]的文章
[Zou, Kuaisheng]的文章
[Lu, Min]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。